Temperature, K | 296 ± 3 | 77.7 ± 0.3 | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
Sample | No. | Site | δ (δext) * | ε {Δ = 2ε} | Γexp | Hext | S | δ | (εext) {Δ = 2ε} | Γexp | Hext | S |
mm s−1 | kOe | % | mm s−1 | kOe | % | |||||||
GC | 1 | Fe3-δO4 | (0.32 ± 0.01) | 0.00 ± 0.01 | 0.57 ± 0.01 | 488.3 ± 0.6 | 43.0 ± 0.3 | 0.47 ± 0.01 | (-0.02 ± 0.01) | 0.40 ± 0.01 | 525 ± 1 | 85.5 ± 0.2 |
(0.56 ± 0.02) | 452 ± 4 | |||||||||||
2 | GC | 0.36 ± 0.01 | − 0.13 ± 0.01 | 0.34 ± 0.01 | 372.3 ± 0.9 | 42.2 ± 0.3 | (-0.10 ± 0.01) | 497.2 ± 0.4 | ||||
3 | Fe+2Oh | 1.05 ± 0.01 | {2.26 ± 0.01} | 0.62 ± 0.02 |  | 6.9 ± 0.2 | 1.32 ± 0.01 | {2.26 ± 0.02} | 0.49 ± 0.03 |  | 6.0 ± 0.3 | |
4 | Fe+3Oh | 0.50 ± 0.01 | {0.51 ± 0.01} | 0.60 ± 0.02 |  | 8.0 ± 0.2 | 0.48 ± 0.02 | {0.94 ± 0.04} | 0.98 ± 0.07 |  | 8.5 ± 0.4 | |
GC–HA10 | 1 | Fe3-δO4 | (0.32 ± 0.01) | 0.00 ± 0.01 | 0.47 ± 0.01 | 496.1 ± 0.7 | 39.2 ± 0.3 | 0.47 ± 0.01 | (− 0.01 ± 0.01) | 0.40 ± 0.01 | 526 ± 1 | 87.3 ± 0.3 |
(0.41 ± 0.01) | 440 ± 2 | |||||||||||
2 | GC | 0.36 ± 0.01 | − 0.13 ± 0.01 | 0.33 ± 0.01 | 376.9 ± 0.6 | 43.1 ± 0.4 | (− 0.10 ± 0.01) | 498.1 ± 0.7 | ||||
3 | Fe+2Oh | 0.95 ± 0.01 | {2.39 ± 0.02} | 0.89 ± 0.04 |  | 7.2 ± 0.3 | 1.32 ± 0.01 | {2.34 ± 0.03} | 0.41 ± 0.04 |  | 3.0 ± 0.3 | |
4 | Fe+3Oh | 0.44 ± 0.01 | {0.69 ± 0.01} | 0.79 ± 0.03 |  | 10.5 ± 0.3 | 0.51 ± 0.02 | {1.07 ± 0.05} | 1.28 ± 0.09 |  | 9.7 ± 0.4 |